Unsaturated polyester resin Ilkester 456

Unsaturated Polyester Resin Ilxter 456

Product Description
Ilxter 456 NS, isophthalic, thixotropic, pre-accelerated, zero-shrinkage unsaturated polyester resin designed for rapid mold production and includes filler.

Features of Ilxter 456 unsaturated polyester resin

• Zero shrinkage
• Processability without waiting for the applied layers to harden
• Low diffusion rate
• Excellent surface quality
• High mechanical and thermal properties

Application areas of Ilxter 456 unsaturated polyester resin

• Mold production
• Lamination applications without shrinkage problems

 Methods of use

• Manual lamination
• Spray

 Packaging details

• Barrel: 230 kg
• Pail: 20 kg

Durability
Durability 6 months from date of production under proper storage conditions.

Storage conditions

• Should be stored in original packaging, at a maximum temperature of 20°C, in a dark and dry place, with the lid tightly closed.
• Avoid exposure to direct sunlight.
• Polyester is flammable and should be kept away from open flames.

  

  Technical characteristics of unsaturated polyester resin Ilxter 456 

  Resin characteristics

  Type of Analysis	Units	Test Method	Amount
  Density, 23°C	g/cm3	ISO 1675	1.12 – 1.14
  Viscosity (23°C), Brookfield RVT, 50 rpm, #4	Centipoise	ISO 2555	800 – 1000
  Styrene Content	Percent	ISO 3251	30 – 32
  Thixotropic Index	mg KOH/g	ISO 2114	2 – 4
  Gel Time	Minutes	İLKALEM TL-06	Summer: 25 – 30 () Winter: 15 – 20 ()
  Peak Exothermic	Celsius	İLKALEM TL-06	120 – 140 (*)

  (*) : 2% MEK-P (Butanox M-60), Polyester Temperature: 23°C, Ambient Temperature: 23°C

  
  Cured Resin Properties
   Pure Resin

   

  Analysis Type	Unit	Test Method	Value
  Tensile Strength	MPa	ISO 527	103
  Tensile Elongation	Percent	ISO 527	3.5
  Tensile Modulus	MPa	ISO 527	6200
  Flexural strength	MPa	ISO 178	175
  Flexural elongation	Percent	ISO 178	5.9
  Flexural modulus	MPa	ISO 178	8000
  Impact resistance	kilojoules per square meter	ISO 180	21
  Hardness (GYZJ 934-1)	–	ASTM-D 2583	40
  Heat distortion temperature	degrees Celsius	ISO 75	80